Morphology of Transverse Cracks at the Corner of Slabs The location of corner cracks in slabs varies depending on the steel grade. For most steel

In the continuous casting process of ultra-low carbon steel, carbonaceous materials in the protective slag penetrate into the surface of the cast billet, increasing the

Based on its function in the core process of continuous casting, mold flux can be divided into two stages: melting and solidification. The first stage

Slab sticking and leakage is the most common (50%-70%) serious accident in slab continuous casting. Its various causes have been detailed above. So how do

Triangular cracks in slabs are a typical internal defect in continuous casting production. They often occur in the “triangular region” (50-150mm from the narrow edge

Formation Mechanism 1. Intrinsic Core Factors: Compositional Segregation and High-Temperature Brittleness (a) Segregation of impurity elements is the fundamental internal cause. Sulfur, phosphorus, carbon, and